LL0209 AA is linear low density polyethylene copolymer containing butane-1 as the co-monomer. LL0209 AA is linear low density polyethylene copolymer containing butane-1 as the co-monomer.In lean blends, this resin offers greater drawdown compared to LDPE neat and produced films are tough with better tear resistance, high tensile stress and good hot-tack properties.
Application:
Shipping sacks Carrier and garbage bags Consumer packaging High clarity film if blended with LDPE
Typical data: (Table)
Property
Unit
Value
Test Method
MFI ( 190oC/2.16 kg )
gr/10min
0.9
ASTM D 1238
Density
gr/cm3
0.920
ASTM D 792
Dart drop impact
gr
130
ASTM D 1709
Tensile strength @ yield | MD
MPa
10
ISO 1184
Tensile strength @ yield |TD
MPa
11
ISO 1184
Tensile strength @ break | MD
MPa
35
ISO 1184
Tensile strength @ break | TD
MPa
28
ISO 1184
Elongation @ break |MD
%
630
ISO 1184
Elongation @ break | TD
%
800
ISO 1184
1% Secant modulus | MD
MPa
190
ISO 1184
1% Secant modulus | TD
MPa
190
ISO 1184
Elemendorf tear strength | MD
MPa
80
ASTM D 1922
Elemendorf tear strength | TD
g/25 m
430
ASTM D 1922
Puncture resistance
N.Cm
585
BPC
LL22501 AA\KJ
Product Description:
22501 is a high stiffness LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose application. Additive: Neutralizer; Calcium Stearate – Antioxidant: DSTDP
Applications:
Blown film grade
Typical Data: (Table)
Property
Unit
Value
Test Method
density
(g/ml)
0.922
ASTM D 1505
MFR(190°C/2.16kg)
(g/10min)
0.95
ASTM D 1238
Dart Impact
(g)
80
ASTM D 1709
Elmendorf Tear MD/TD
(g)
105/460
ASTM D 1922
Tensile strength at yield MD/TD
(MPa)
13/12.5
ASTM D 882
Tensile strength at Break MD/TD
(MPa)
45/30
ASTM D 882
Ultimate Elongation MD/TD
(%)
680/780
ASTM D 882
2% Secant modulus MD/TD
(MPa)
200/240
ASTM D 882
Haze
(%)
21
ASTM D 1003
Gloss 45°
(%)
38
ASTM D 2457
Physical properties obtained on 25 micron film, obtained on Collin 25, B.u.R. 2.5:1, Temp. Profile 155^-190°C this data are typical values and are not to be construed as product specifications.
Packing: 25 Kg plastic bag
LL22B02 AA
TYPICAL PROPERTIES
TEST METHOD(DIN)
UNIT
VALUE
MFI@190 ° C,2.16kg
ISO 1133
gr/10min
1.8 – 2.1
Density
ISO 1183
gr/ml
0.920 – 0.923
Tensile STR.@Yield
ASTMD882-10
Mpa
18 – 21
Tensile STR.@ Break
ASTMD882-10
Mpa
54 – 36
Elong.@ Break
ASTMD882-10
%
780 – 990
Elmendorf Tear Strength
ASTMD1922-09
g/25 μm
35 – 325
Main application & Characteristics:
Typical applications are:
for use in lean and rich blend blown film application such as overwrap,counter bags,shrink film and boil in the bag applications
artificial grass
LL22B03 AA
TYPICAL PROPERTIES
TEST METHOD(DIN)
UNIT
VALUE
MFI@190 ° C,2.16kg
ISO 1133
gr/10min
2.8 – 3.1
Density
ISO 1183
gr/ml
0.920 – 0.923
Tensile STR.@Yield
ASTMD882-10
Mpa
18 – 21
Tensile STR.@ Break
ASTMD882-10
Mpa
54 – 36
Elong.@ Break
ASTMD882-10
%
780 – 990
Elmendorf Tear Strength
ASTMD1922-09
g/25 μm
35 – 325
Main application & characteristics:
Typical application are:
Hight stiffness blown films; blending
Lamination / film
miscellaneous,
General purpose cast stretch films
also W&C blend ,cast stiff film,diaper backing films
LL0220 AA\KJ
Product Description: LL0220KJ is linear low density polyethylene copolymer containing butene-1(C4) as comonomer. It is suitable for blending with conventional LDPE for blown film applications. Film made from pure LL0220KJ has the following advantages over LDPE: Good balance of mechanical properties, good optical properties and easy opening properties in 2 layer film.
Applications: Light and medium duty films with good optical properties.
Typical data: (Table)
PROPERTY
UNIT
METHOD
VALUE
MELT FLOW INDEX(2.16KG)
g/10min
ASTM
2.4
DENSITY
gr/cm3
ASTM
0.921
VICAT SOFTENING POINT
°C
ASTM
100
FILM**
DART DROP IMPACT
METHOD A
GR
ASTM
90
TENSILE STRESS AT YEILD
MD/TD
MPA
ASTM D-882
10/11
TENSILE STRESS AT BREAK
MD/TD
MPA
ASTM D-882
30/25
ELONGATION AT BREAK
MD/TD
%
ASTM D-882
1000/110
HAZE
–
%
ASTM
0
GLOSS(45°)
–
%
ASTM
30
*All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications) **38|im film, 2.5:1 blow up ratio, 225°c melt temperature, MD: Machine Direction, TD: Transverse Direction Grade Suffix (Additives Indication): KJ: GENERAL ANTIOXIDANT WITH SLIP AGENT/ANTIBLOCKING AGENTS