LH0075 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. Film made from LH0075 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. It can be processed on automatic machines. It possesses good dimensional stability. LH0075 is chiefly recommended for extrusion of blown film. It is suitable for shrink film having a high resistance to hole formation and high degree of shrinkage on cooling. LH0075 contains antioxidant.
LH0075 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. Film made from LH0075 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. It can be processed on automatic machines. It possesses good dimensional stability. LH0075 is chiefly recommended for extrusion of blown film. It is suitable for shrink film having a high resistance to hole formation and high degree of shrinkage on cooling. LH0075 contains antioxidant.
Applications:
Carrier bags Shrink film Industrial film Dust bin liners large bottles Blow moulding of small containers Packaging of pharmaceutical products.
Typical Data: (Table)
PROPERTY
METHOD
UNIT
VALUE
M.F.I (190°C/2.16 kg)
ASTM D 1238
gr/10 min
075
Density
**TSTM 209B
gr/ml
0.9210
Vicat softening point
ASTM D 1525
°C
94
Elongation at break (MD)
ASTM D 882
%
300 min.
Elongation at break (TD)
ASTM D 882
%
450 min.
Tensile at break (MD)
ASTM D 882
Kg/cm2
170 min.
HDT
ASTM D 648
°C
33
Dart impact
ASTM D 1709
gr
120 min.
* Typical values not to be construed as specifications.
** TSTM = Toyo Soda Standard Test Method The above data are typical laboratory average. They are intended to serve as guides only
LF0190
Product Description:
LF0190 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties.
Applications:
General purpose film and for lamination
Typical Data: (Table)
PROPERTY
METHOD
UNIT
VALUE*
MFR (190°C/2.16 kg)
ISO 1133
Dg/min
1.9
Density
ISO 1183(A)
g/cm3
0921
Impact Strength
ASTM D 4272
KJ/m
20
Tear Strength (TD)
ISO 6383-2
. kN/m
25
Tear Strength (MD)
ISO 6383-2
kN/m
70
Yield Stress (TD)
ISO 527
MPa
11
Yield Stress (MD)
ISO 527
MPa
11
Strain at Break (TD)
ISO 527
%
500
Strain at Break (MD)
ISO 527
%
100
Modulus of Elasticity (TD)
ISO 527
MPa
190
Coefficient of friction
ASTM D 1894
—
>1
Modulus of Elasticity (MD)
ISO 527
MPa
190
Blocking
Sabtec
g
20
Re-blocking
Sabtec
g
50
Haze
ASTM D 1003A
%
12
Gloss
ASTM D 2457
%
53
Clarity
Sabtec
mV
26
* Typical values not to be construed as specifications.
L2102TX00
Product Description:
LDPE 2102TX00 GP film
Application:
• It is used in wide range of widths and thicknesses e.g. for punches, bags, liners and lamination film.
Typical data. (Table)
Property
Unit
Value
Method
Physical
MFI
Dg/m in
1.9
ISO 1133
Density
kg/m*
921
ISO 1183 (A)
optical
Haze
%
11
ASTM D1003A
Clarity
mV
29
DSM METHOD
Gloss
%
50 ±5
ASTM D2457
Formulation
Anti-oxidant
ppm
600±60
DSM METHOD
Anti-block
ppm
–
slip
ppm
–
Film property
Impact Strength
kJ/m
26
ASTM D4272
Tear Strength TD
KNf m
25
ISO 6383-2
Tear Strength MD
KNf m
60
ISO 6383-2
Yield Stress TD
MPa
11
ISO R527-1
Yield Stress MD
MPa
13
ISO R527-1
Tensile Strength TD
MPa
20
ISO R527-1
Tensile Strength MD
MPa
–
ISO R527-1
Elongation at break TD
%
>500
ISO R527-1
Elongation at break MD
%
>150
ISO R527-1
Modulus of elasticity TD
MPa
200
ISO R527-1
Modulus of elasticity MD
MPa
190
ISO R527-1
Coefficient of friction
%
>1.0
ASTM D1894
LF0200
Product Description:
LF0200 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. Film made from LF0200 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. Its toughness bears even in cold temperatures. The film can be sealed on all types of machines. The film possesses good dimensional stability and is resistant to tearing and breaking. LF0200 contains antioxidant.
Applications:
General purpose bags, Packaging of mechanical parts Industrial film, Carrier bags large bottles, Coextruded milk bags, low tension power cables insulation and industrial injection moulding.
PROPERTY
METHOD
UNIT
VALUE
M.F.I (190°C/2.16 kg)
ASTM D 1238
gr/10 min
2
Density
**TSTM 209B
gr/ml
0.920
Softening point
ASTM D 1525
°C
94
Haze
ASTM D 1003
%
15 max.
Gloss at 60
ASTM D 523
Gu
60 min.
Elongation at break (MD)
ASTM D 882
%
330 min.
Elongation at break (TD)
ASTM D 882
%
600 min.
Tensile at break (MD)
ASTM D 882
Kg/cm2
160 min.
Dart impact
ASTM D 1709
gr
100 min.
* Typical values not to be construed as specifications.
** TSTM = Toyo Soda Standard Test Method The above data are typical laboratory average. They are intended to serve as guides only